| (2) Corrosion at cross sections of coating layer |
| • |
Photo-7 shows cross sections of coating layer after 10-year atmospheric exposure test.
(See page 16-17) |
| • |
Table-7 shows the condensation of results: |
|
| a) |
Singapore: Coating layer of W.R.Alstar has not corroded much and remains in good condition. As to 55% Al-Zn, Zn-rich layer (phase) in coating layer has corroded and some blisters of the coating layer noted. As to Galvanized, zinc coating layer has completely vanished. |
| b) |
Manila: Coating layer of W.R.Alstar has not corroded much and remains in good condition. As to 55% Al-Zn, Zn-rich layer (phase) in coating layer has corroded and some blisters of the coating layer noted. With Galvanized, much of the zinc coating layer has vanished. |
|
|
Table-7. Evaluation of corrosion at cross sections of coating layer after 10-year atmospheric exposure tests.
|
|
|
Photo-7-1. Cross section of several coated steel sheet after 10-year atmospheric exposure tests
|
 |
Photo-7-2. Cross section of several coated steel sheet after 10-year atmospheric exposure tests
|
|
 |
| 010 |